PostPosted: Sun 03 Nov, 2019 7:57 am    Post subject: Case hardening using nitrides         Reply with quote

Nitrification is the process of using nitrogen to case harden metal. Today it is usually done with ammonia gas but an ammonium salt bath also works. We have texts telling us that some sword smiths quenched their blades in urine. Stale urine contains a significant amount of ammonium and so it might be possible to use it to nitrify a blade.

My question is whether we have any physical evidence to support the above. Are there any extant swords showing evidence of nitride case-hardening rather than the usual carbide case-hardening?

Author: Bronze Age Military Equipment, Pen and Sword Books
View user's profile Send private message
Lihan Hauk





Joined: 28 Jan 2008

Posts: 9

PostPosted: Sun 03 Nov, 2019 11:35 am    Post subject:         Reply with quote

Hello,
look at Wieland the blacksmith! that's an old germanic legend. He files up a sword that he doesn't think is good enough. Bakes it in bread and feeds it to geese. Then he melts the dung in the oven and makes a new sword out of it. Scientists have repeated the experiment and found that it was a method to add nitrate to the steel. there are also reports that the same methods were used in ancient Turkey.
View user's profile Send private message
Dan Howard




Location: Maitland, NSW, Australia
Joined: 08 Dec 2004

Spotlight topics: 2
Posts: 3,636

PostPosted: Sun 03 Nov, 2019 1:54 pm    Post subject:         Reply with quote

I know that it works on a theoretical level and have read many swordsmith anecdotes in which the result may have nitrided the blade. What I want is physical evidence. I'm looking for a metallurgical analysis of a sword, which demonstrates that the blade was case hardened with nitrides rather than carbides. Without this it is all speculation.
Author: Bronze Age Military Equipment, Pen and Sword Books
View user's profile Send private message
James Arlen Gillaspie
Industry Professional



Location: upstate NY
Joined: 10 Nov 2005

Posts: 587

PostPosted: Mon 04 Nov, 2019 8:10 am    Post subject:         Reply with quote

Due to how shallow the depth of the nitriding process tends to be, it will be very difficult find a surviving example due to corrosion loss and even 'cleaning'.
jamesarlen.com
View user's profile Send private message Visit poster's website
Dan Howard




Location: Maitland, NSW, Australia
Joined: 08 Dec 2004

Spotlight topics: 2
Posts: 3,636

PostPosted: Mon 04 Nov, 2019 2:42 pm    Post subject:         Reply with quote

James Arlen Gillaspie wrote:
Due to how shallow the depth of the nitriding process tends to be, it will be very difficult find a surviving example due to corrosion loss and even 'cleaning'.

Yep, I realise that, but until we find physical evidence supporting its historical practice, the concept remains speculative.

Author: Bronze Age Military Equipment, Pen and Sword Books
View user's profile Send private message


Display posts from previous:   
Forum Index > Off-topic Talk > Case hardening using nitrides
Page 1 of 1 Reply to topic
All times are GMT - 8 Hours

View previous topic :: View next topic
Jump to:  
You cannot post new topics in this forum
You cannot reply to topics in this forum
You cannot edit your posts in this forum
You cannot delete your posts in this forum
You cannot vote in polls in this forum
You cannot attach files in this forum
You can download files in this forum






All contents © Copyright 2003-2024 myArmoury.com — All rights reserved
Discussion forums powered by phpBB © The phpBB Group
Switch to the Basic Low-bandwidth Version of the forum