Lancelot Chan
Industry Professional
|
 Posted: Wed 03 Dec, 2014 6:52 am Post subject: Testing Alvin Alejandro Atencio made DS |
 |
|
http://youtu.be/9sJyUYr6sfo
Testing out the second Alvin-made DS. The first one came dull and with a twisted blade. The first one also suffered microchip after test cutting on wet newspapers. So after some communication with the smith, it was sent back to him. He made me a new, better one.
The second one features a sharp blade out of the box, straight and good. It's made very accurately to the spec., except the guard being several mm shallower. It's definitely the most accurate DS I've received so far, and the lightest among the three-some.
However, the hardness isn't very high compare to the Tinker-made and John Lundemo-made one, spotting low at 40 HRC to high at below 55HRC. Edge got dulled after test cutting on newspapers. No microchip this time. It's acceptable to me, at the given price and shipping time. I don't expect a super sword at that cost.
One interesting note is that the blade has a hole in it that was filled with a harder steel. Strange huh? I don't think it will affect functionality, and I think it's from the leaf-spring application of the steel. Just the first time I saw something like this though.
Ancient Combat Association —http://www.acahk.org
Realistic Sparring Weapons — http://www.rsw.com.hk
Nightstalkers — http://www.nightstalkers.com.hk
|
|
   |
 |
|
Jeffrey Faulk
|
| Posted: Wed 03 Dec, 2014 8:11 am Post subject: |
|
|
Is this a sword design that you own? Just curious because I am not sure the other smiths would approve if it's their design...
As for the filled hole in the steel, it should not affect functionality in any manner that you would notice if it has been done well. The welded area around it might be slightly stiffer than the rest, but if the blade was well annealed after the welding was done and re-tempered, it should not have been an issue.
|
|
|
|
|
Lancelot Chan
Industry Professional
|
| Posted: Wed 03 Dec, 2014 8:19 am Post subject: |
|
|
Yes, I own the design.
Thanks for the confirmation on the steel weld.
| Jeffrey Faulk wrote: | Is this a sword design that you own? Just curious because I am not sure the other smiths would approve if it's their design...
As for the filled hole in the steel, it should not affect functionality in any manner that you would notice if it has been done well. The welded area around it might be slightly stiffer than the rest, but if the blade was well annealed after the welding was done and re-tempered, it should not have been an issue. |
Ancient Combat Association —http://www.acahk.org
Realistic Sparring Weapons — http://www.rsw.com.hk
Nightstalkers — http://www.nightstalkers.com.hk
|
|
|
|
|
Ian Hutchison
Location: Louisiana / Nordrhein-Westholland Joined: 27 Nov 2007
Posts: 626
|
| Posted: Wed 03 Dec, 2014 6:18 pm Post subject: |
|
|
| Lancelot Chan wrote: | Yes, I own the design.
Thanks for the confirmation on the steel weld.
| Jeffrey Faulk wrote: | Is this a sword design that you own? Just curious because I am not sure the other smiths would approve if it's their design...
As for the filled hole in the steel, it should not affect functionality in any manner that you would notice if it has been done well. The welded area around it might be slightly stiffer than the rest, but if the blade was well annealed after the welding was done and re-tempered, it should not have been an issue. |
|
Lancelot,
I think it is a pretty neat idea to have the same sword design produced by different smiths, it would be interesting to compare the various outcomes!
'We are told that the pen is mightier than the sword, but I know which of these weapons I would choose.' - Adrian Carton de Wiart
|
|
|
|
|
Lancelot Chan
Industry Professional
|
| Posted: Wed 03 Dec, 2014 7:05 pm Post subject: |
|
|
Oh definitely! And the quality and the characteristics of each smith still show in this "high accuracy" project, because the specification was very exact.  It's a big test of "grind-fu", in addition to heat treatment control.
| Ian Hutchison wrote: | | Lancelot Chan wrote: | Yes, I own the design.
Thanks for the confirmation on the steel weld.
| Jeffrey Faulk wrote: | Is this a sword design that you own? Just curious because I am not sure the other smiths would approve if it's their design...
As for the filled hole in the steel, it should not affect functionality in any manner that you would notice if it has been done well. The welded area around it might be slightly stiffer than the rest, but if the blade was well annealed after the welding was done and re-tempered, it should not have been an issue. |
|
Lancelot,
I think it is a pretty neat idea to have the same sword design produced by different smiths, it would be interesting to compare the various outcomes! |
Ancient Combat Association —http://www.acahk.org
Realistic Sparring Weapons — http://www.rsw.com.hk
Nightstalkers — http://www.nightstalkers.com.hk
|
|
|
|
|
Lancelot Chan
Industry Professional
|
|
|
|
|
Lancelot Chan
Industry Professional
|
|
|
|
|
Lancelot Chan
Industry Professional
|
|
|
|
|
|
|
You cannot post new topics in this forum
You cannot reply to topics in this forum
You cannot edit your posts in this forum
You cannot delete your posts in this forum
You cannot vote in polls in this forum
You cannot attach files in this forum
You can download files in this forum
|
All contents © Copyright 2003-2024 myArmoury.com — All rights reserved
Discussion forums powered by phpBB © The phpBB Group
Switch to the Basic Low-bandwidth Version of the forum
|
This is a standard topic