[Chad Arnow]

[Richard Fay]

Chad,
Thanks for pointing out the bibliography! I used it to add some more books to my list, and I also added a few I forgot about. I hope it's alright that I added some general medieval histories and biographies. I think an understanding of the society and culture in the middle ages helps add to knowledge about medieval arms and armour. Besides, many of my books have at least a picture or two, or entry or two, of armour or weapons!
I can't believe I read most of those books, and medieval arms and armour is only one of my interests!
Stay safe!

[Chad Arnow]

[Richard Fay]

Hello all!
Just when you thought I was done with this topic, I thought I would post some pictures of the swords I mentioned in earlier posts. After all, a picture's worth a thousand words. Hope it's okay to use these!

[Sean Flynt]

Another point to consider when discussing the wisdom of using copper alloys in life or death situations:

Bronze armour...and not just in the bronze age.

Nobody would argue that the Romans used bronze scale armour because they had no ferrous alternatives. Clearly, the material was considered appropriate for defensive use in some contexts (lorica squamata- http://en.wikipedia.org/wiki/Lorica_squamata ). And didn't gladii often feature a bronze plate between blade and guard? Doesn't that count as a front-line use of copper alloy post-bronze age?

[Richard Fay]

Hello all!

Chad Arnow wrote:

[Chad Arnow]

[Sam Gordon Campbell]

Sorry if this sounds un-scholarly, but brass/bronze coloured hilts appear in things like the Maciejowski Bible, and though this may be pure artistic licence, could it not perhaps be the case that the depictions may indeed have some bases in reality?

BTW: I think brass/bronze hilts look oh so more stylish than iron/steel

[Nicholas A. Gaese]

Good day Gents!

While everyone is talking about the use of bronze/brass in the use of sword and knife hilts in Europe, I thought that maybe I should dig up some info on the use of said metals from their neighbors to the south-east.

It seems that from what I gathered from my university courses on Middle-Eastern history, bronze particularly remained a very popular material for weapons and and everyday items right up to the 20th century. While regrettably the books and sources available to us do not go into much on period arms and armor, they provide various examples of period artwork. In one book, "Cambridge Illustrated History: Islamic World" they often show swords with hilt components made entirely of bright yellow bronze, this is often a depiction of 15th century Ottoman Turks at war, particularly with the sacking of Byzantium where various swords can be seen. Another depiction I found was one of the Mughal Emperor Shah Jahan of 1640 with his personal Guard at his court, possibly in Delhi. All of the Shah's guard were bearing "gurz" (maces) made entirely of bronze, and also wearing swords with nearly all of the hilt components in bronze, except one where the entire hilt appears bright red (copper perhaps?). Now as far as physical evidence is concerned, most of the actual swords that ive seen have embellished iron furniture so maybe in the depictions it might be as such, but I have also seen plenty with pure bronze so it could go either way. As for the use of brass im at a loss. I heard once during one of our professor's lectures he mentioned something about latten being used by lesser nobles to embelish sword kartouches and inscriptions instead of gold at times, other then that ive heard little about the use of brass. Perhaps brass was used in embellishing hilt furniture as well as bronze? This would add the nifty advantage of rust-proofing sword furniture without compromising the guard or pommels integrity, I know of many examples of this with Indian Tulwars.

Obviously Mr. Kourasani's book "Arms and Armor of Iran" will be a better source, as that is the main subject of the book, however the big price tag ( as well as the poor student lifestyle) keeps me from getting a copy anytime soon

Best Regards

Nicholas

[Chad Arnow]

[J.D. Crawford]

I rather like the look of brass furniture on certain swords, In fact I have MRL's two-hand claymore propped in the corner of my dining room and even the wife seems to like this heavy but attractive beast.

But I got turned off of brass guards for functional use early on. I was trying to do something ridiculous (that I saw on a movie) with one of my first swords. I dropped the sword - and bent the thin brass guard. I ended up bending the other side to make them match. That's when I realized how flimsy it really was. My feeling was that a good sword stroke would have cut right through that guard. (I eventually gave that sword to a friend who was going through a difficult time - nothing better than a sword to cheer up a fellow).

So from a functional perspective I guess it also depends on how thick the guard is - I would think that a thick chunky brass guard would be fine, if it doesn't add too make much weight and still looks balanced to the eye. Perhaps that the fundamental problem with brass - one will have to add more weight to get the same amount of strength.

But back to history - I will ask a question here that I asked on another 'brass thread' and I don't think it was answered: Is it true that brass was used more often in damp climates like Scotland? I mean, it makes sense, but can anyone confirm this?

[Jared Smith]

[Chad Arnow]

I think that some people think all brass is the same. As with any metal (think steel), there are various alloys and ratios of elements. As a trombonist, I come into contact wth a variety of brass alloys every day and I can tell you they aren't all the same. Some are harder than others.

My guess is that the kind of companies that regularly use brass use the cheapest alloys they can buy, and those all seem to be soft.

I have said all along that I think steel is a better choice. However, brass was used in at least some cases by people whose lives depended on their weapons more than many of us today.

[Jared Smith]

I would think historical blade furniture was frequently made in bronze because of the viability of casting "to fit" based upon molds of tang and blade base areas, rather than by forging. High copper-zinc bronze alloys would work, even with impurities (which were probably present in abundance.) I find this option attractive today as I consider the alternatives of special swages-drifts for punching, hot work grade fly press, and other things that would be best for forming furniture from steel. Casting of brasses/ bronzes takes much less of an investment, and less shop space to do in small scale project terms.

[A. Jake Storey II]

Two things occurred to me. I could see people using copper alloys because of rationing. If, because of the movements and position of approaching enemy armies cutting of some of the iron/steal supply, they could use copper alloys for some of the furniture of the weapons to make sure they had enough iron and steal for armor and blades. Also, what about rapiers and small swords? They wouldn't be receiving, in most cases, as much of a beating as a longsword or side sword might. So brass and other copper alloys could be a more acceptable choice for them.

[Naythan Goron]

hello all
i just thought i would pitch in my 2 cents on this topic as im greatly interested in swords that do not have iron fittings (being as about half the swords i own do not have iron/steel fittings) windlass recently discontinued a sword that i managed to add to my collection called the Sword of Cortenuova (as seen on kultofathena http://www.kultofathena.com/product.asp?item=...Cortenuova ) and i must say i like it, the brass looks good and its one of the best handling swords ive got. however im almost positive that if a sword came sliding down my blade and struck the cross guard i can probably kiss my hand good bye. so this rises into question in my mind if brass, copper, tin, silver etc were used as hilt components for swords, how common would hand injures sustained by a sword chopping though your cross guard been? not to get off topic from the thread or anything but i think that this too is something to look at when using not so very hard items in cross guards.

[A. Jake Storey II]

Naythan, I doubt there was much problem of them hacking through the hilt parts. Movies and books love to exagerate how much damage a sword can do. Denting, bending, some cracking, maybe snapping parts
, or grooving are about what you would be getting. Even then, the sword would be stopped, slowed, and/or redirected by the collision; so, I don't think injuries because of the sword getting 'through' would be a problem, though injuries from them getting around a, now, mangled guard would be the real issue.

[Toke Krebs Niclasen]

The alloy used for cannons were at the time stronger than cast iron, or at least not prone to catastrophic failure.
It was also a lot more expensive so not all used it.
http://en.wikipedia.org/wiki/Gunmetal

I have seen a few examples where brass looked good on a sword, but are generally against it for aesthetic reasons.

[Jeroen Zuiderwijk]

[Jean Thibodeau]