Sean Flynt wrote: |
But we know that MRL can do better, so it isn't a matter of financial limitation. As for the example you cite here, that seems to be one of their better recent offerings ("better" in this context meaning it's based on a documented original sword). I look forward to seeing that one steeply discounted. |
I guess it really is a matter of taste, that 'German bastard sword' has the 'sharpened crowbar' look to me, the newer one looks at least in the ballpark of being something you could actually use in a fight, ricasso or no.
J
Books and games on Medieval Europe Codex Integrum
Codex Guide to the Medieval Baltic Now available in print
|
|
|
|
Sean Flynt
|
|
|
|
Jean Thibodeau
|
Posted: Tue 30 Jan, 2007 1:02 pm Post subject: |
|
|
Richard Fay wrote: | Oh, one other point, wouldn't the ridge section of the Type XIV in the Metropolitan Museum of Art be raised as compared to the fuller section? Since the fuller is a depression, and the ridge a rise, I think there would have to be some thickening at the point where fuller gives way to ridge, wouldn't there? It's hard to interpret a sword just from a photo, but the fuller looks "lower" and the ridge "higher", if you know what I mean. Just a thought!
Stay safe! |
Richard you are correct if the blade is first ground as a full length diamond section, but if instead imagine it being ground initially with a flat where the fuller is later ground: The thickness of the flat being as thick as the spine of the diamond section.
Then if the fuller is ground into this flat leaving the ridge line as high as the spine you wouldn't get the reinforced point effect.
( Note: The fuller could be ground in first or after the distal taper but in period the sword would probably be forged before any grinding. Oh, and grinding from flat bar stock in the modern context wouldn't be done in period I'm 99% sure. )
Now one might want a very small thickening of the point but it's different if it just happens sort of by accident.
Oh, and I also think that we shouldn't be too critical of decent but lower end swords.
( But still worth discussing design in itself )
I will also agree with Chad that it seems like MRL uses the same approach of diamond sections for everything and they probably use the same basic steel stock thickness for almost everything ? ( Or only a couple of thicknesses like 3/16" or 1/4" )
You can easily give up your freedom. You have to fight hard to get it back!
|
|
|
|
|
You cannot post new topics in this forum You cannot reply to topics in this forum You cannot edit your posts in this forum You cannot delete your posts in this forum You cannot vote in polls in this forum You cannot attach files in this forum You can download files in this forum
|
All contents © Copyright 2003-2024 myArmoury.com All rights reserved
Discussion forums powered by phpBB © The phpBB Group
Switch to the Basic Low-bandwidth Version of the forum
|