side effects of heat-treatment?
I just have a small query about the forging of arms and armour.

Upon quenching the sword ,lets say, is there a possibility of warping the piece.

Of course the properties change (hard, brittle, etc.), but I am asking a topological change may occur.

Thanks in advance.


Josh
Yes, it is possible with thin materials at higher temps required to achieve modern high-strength states. Lower carbon alloys as used in period really would not have seen these higher temps, so they would have had a low likely-hood of deforming. Basically, there were probably no worries with properly tempered period armour or arms. Quarter inch thickness is substantial enough not to be bothered by warping in practically all cases, and that is the approx. thickness of most swords. An 18 guage armour made from 4130 (standard chro-molly) heat treated to the approx. 200 ksi and above range might encounter problems with slight deformation, if a high-temp heat-treating jig was not used. I might be slightly off on some of the numbers, but the gist is correct. Hope that helped some... :)
Small variations in grain structure, uneven surface finish and uneven heating of the steel prior to quenching will very easily lead to warping, distortion or even cracking.
Whatever work has been done to the piece before heat treat will have an effect on final outcome. Even cold work like filing can build stress in the surface of the steel that might provoke bending in heat treat if not normalized properly.
Normalization is absolutely critical for good results.
Even then, a long thin object like a swordblade very easily takes a set in heat treat. What is really very minimal in a short blade like a knife will be multiplied many times in a long sword blade.
There will normally be some slight straightening to do each and every time after heat treat. Sometimes it is very minute, sometimes more severe.
I do not think this is any different today than it was in ancient times. Even if you have blades that are partly made of iron that do not take hardness in a quench, you can still get warpge in the stel present.
When you heat treat swordblades, you quickly learn techniques to straighten.

An even surface all over the blade and an exact edge thickness on both sides from base to point will help minimize warpage. It is still paramount to apply heat carefully and evenly.

Also with armour there can be distortion.
You can use the rivet holes in the plate to fasten fixtures to minimize warpage. I do not make armour these days, so others might provide more info here.
Very intresting.

Thanks for the information.

josh

Page 1 of 1

Jump to:  
You cannot post new topics in this forum
You cannot reply to topics in this forum
You cannot edit your posts in this forum
You cannot delete your posts in this forum
You cannot vote in polls in this forum
You cannot attach files in this forum
You can download files in this forum




All contents © Copyright 2003-2006 myArmoury.com — All rights reserved
Discussion forums powered by phpBB © The phpBB Group
Switch to the Full-featured Version of the forum