Alexander Hinman




Location: washington, dc
Joined: 08 Oct 2005
Reading list: 50 books

Posts: 180

PostPosted: Mon 27 Nov, 2006 3:29 pm    Post subject: Flex and Durability of Iron Cored Swords         Reply with quote

In Alan Williams' chapter (?) of Companion to Medieval Arms and Armour, titled 'Metallurgy of Medieval Arms and Armour', he analyses a sword from the Mary Rose, pointing out that it is effectively steel welded to an iron core, and showing the purely martensitic microstructure of the edge. He also gives hardness values for various points in the sword, ranging from VPH 592 near the edge (about 55 HRC) to VPH 287 (28 HRC) near the core.

He also shows a chart that suggests that a quenched (and untempered) piece of 30 point (that is, .3% carbon) steel would give the same hardness (590 VPH). Since the edge is purely martensitic, this suggests to me that the steel was of a very low carbon content.

My question is, how functional would such a low-carbon weapon be? And more importantly, how does the iron core of case carburised or otherwise steel-encased sword affect its a) Durability, and b) its flex? Does it make it more likely to take a set (than monosteel)? To fracture? What effects does a lack of tempering have?

I'm tempted to think these swords (hardened, low carbon exterior and iron core) would be more likely to take a set and more likely to fracture, but that's just my assumption. Case-carburised swords, with their high-carbon exterior are well beyond my guesses, however.
View user's profile Send private message
Craig Johnson
Industry Professional



Location: Minneapolis, MN, USA
Joined: 18 Aug 2003
Likes: 16 pages
Reading list: 20 books

Spotlight topics: 1
Posts: 1,421

PostPosted: Mon 27 Nov, 2006 3:43 pm    Post subject: Iron/Steel Blades         Reply with quote

Good Question Alexander

The period blades have a tendency to be more like a rough mix of carbon content than a set level. The result is the hardness will vary in a piece.

The case carburized and iron core pieces would have a tendency to be more ductile, i.e. possibly take a set easier but would allow an easier bend back to shape and would not be prone to fracture as the iron with no carbon in it would be very malleable.

As these swords are made from steel/iron mixes that are small batch smelts each sword would probably have a slightly different make up on the molecular level.

That’s the quick answer. Happy The structure of period blades can be very complex and I am working on an article that will deal with some of the hardness issues.

Best
Craig
View user's profile Send private message Send e-mail Visit poster's website


Display posts from previous:   
Forum Index > Historical Arms Talk > Flex and Durability of Iron Cored Swords
Page 1 of 1 Reply to topic
All times are GMT - 8 Hours

View previous topic :: View next topic
Jump to:  
You cannot post new topics in this forum
You cannot reply to topics in this forum
You cannot edit your posts in this forum
You cannot delete your posts in this forum
You cannot vote in polls in this forum
You cannot attach files in this forum
You can download files in this forum






All contents © Copyright 2003-2024 myArmoury.com — All rights reserved
Discussion forums powered by phpBB © The phpBB Group
Switch to the Basic Low-bandwidth Version of the forum