How plate amour be repaired historically?
Hi guys, there's a question I wonder and have never see discussed before( forgive me if I'm wrong and please give me the link of the related topic): How plate armour be repaired? they are combat tools and must be exposed to continuous strike and damage ,and iron or steel plate 1-2mm thick is not immune to such damage completely, even the man in the armour were saved from being hurt, there must be dent , hole on it ,and must be repaired.

In the case of mail \lamellar\coat of plates the solution is relatively easy, just replace the damaged ring or small plates, but in plate armour, some parts are large and expersive to be replaced altogether, especially the breastplate ,which are most possible to be striked , won't that be a serious disadvantage compare to mail, lamellar or brigandine in cost, when common soldiers rely goverment to provide their armour? If not replaced completely, are technics such as patching used?

Any opinion on the question is OK , but more historical evidences are most welcomed.
They had a type of "spackle", made from casein glue and a few other ingredients, that was used to patch holes in metal plate.
Dan Howard wrote:
They had a type of "spackle", made from casein glue and a few other ingredients, that was used to patch holes in metal plate.

thanks Dan, that's an interesting method I didn't expect. Any further historical references? How about the strength of that kind of patch?
They also used metal patches and cover plates. We had some breastplates that had been shot through from the 17th century and they simply had a patch put in from the back, hammered and riveted in. Once polished it was not even something you could see.

RPM
Copper brazed repairs (often with a backing plate, the whole shebang hot riveted in while the copper was molten) were very common. It makes for an extremely strong repair, though it would require retempering good steel armour, unless it's Italian (pearlitic microstructure). Not a big deal, since brazing heat is right for hardening anyway!
Dan Howard wrote:
They had a type of "spackle", made from casein glue and a few other ingredients, that was used to patch holes in metal plate.


You having a bad week or something, Dan? :confused:
James Arlen Gillaspie wrote:
Copper brazed repairs (often with a backing plate, the whole shebang hot riveted in while the copper was molten) were very common. It makes for an extremely strong repair, though it would require retempering good steel armour, unless it's Italian (pearlitic microstructure). Not a big deal, since brazing heat is right for hardening anyway!

Thanks, brazing is another technic I can easily understand(appeared in the movie A Knight's Tale), but again is there any historical evidence? like a museum speciman threated exactly so? As far as I saw, most museum armour don't even have slight battle damage~
Greetings!
This question always kept me thinking, and one day in the Arsenal of Graz, I saw the answer! (Please note the picture!) Sorry for the poor quality of the photo, it was made in a dark room with my phone, but still, it could give you an idea! :)
John


 Attachment: 147.49 KB
Repaired armour from Graz [ Download ]
János Sibinger wrote:
Greetings!
This question always kept me thinking, and one day in the Arsenal of Graz, I saw the answer! (Please note the picture!) Sorry for the poor quality of the photo, it was made in a dark room with my phone, but still, it could give you an idea! :)
John


I've seen a very similar repair at a museum in Rothenburg ob der Tauber, Germany. I'll look through my old photographs to see if I have a snapshot.

Page 1 of 1

Jump to:  
You cannot post new topics in this forum
You cannot reply to topics in this forum
You cannot edit your posts in this forum
You cannot delete your posts in this forum
You cannot vote in polls in this forum
You cannot attach files in this forum
You can download files in this forum




All contents © Copyright 2003-2006 myArmoury.com — All rights reserved
Discussion forums powered by phpBB © The phpBB Group
Switch to the Full-featured Version of the forum