PostPosted: Thu 15 Jan, 2009 2:20 pm    Post subject: pattern welding without strikers or trip hammer?         Reply with quote

I am wondering what the maximum sized (cross section) billet (1085/95 & 15N20 strips) is that one should undertake for drawing out by hand using just anvil (200 lb) and hammer (3 lb)? My intent is to make a twisted core with layered laminated edges. Also, to be traditional, would migration era smiths have worked with similarly small strips and then welded the strips together without a team of strikers?

In my case, the desire to do it this way is mostly driven by lack of appropriate space and budget for a modern air powered hammer. I sought to enroll in a local class for fabrication of a "tire hammer" (uses a spare tire hub as a cam to drive 50 to 75 lb hammers), but there was not enough local enrollment for the class to be held.

Absence of evidence is not necessarily evidence of absence!
View user's profile Send private message
Michael Pikula
Industry Professional



Location: Madison, WI
Joined: 07 Jun 2008

Posts: 411

PostPosted: Thu 15 Jan, 2009 3:04 pm    Post subject:         Reply with quote

As someone who started making pattern weld with a coal forge and hand hammering, I would say that 1 - 1.5 inches wide, 5 inches long, and around 1.5 - 2 inches tall should ge a good starting point.

I don't know if it is historically to combine two billets to increase layer count and size, but I find it much better to work two billets and then weld them together if I need a larger billet. If you are working a huge billet you are going to end up fighting with it and might end up scraping more material and time then if you take your time, work small, and then add on to get the size/layers that you need.
View user's profile Send private message Visit poster's website
Jared Smith




Location: Tennessee
Joined: 10 Feb 2005
Likes: 1 page

Spotlight topics: 3
Posts: 1,532

PostPosted: Thu 15 Jan, 2009 3:09 pm    Post subject:         Reply with quote

Thanks for the input Michael.
I would like to end up with twisted core strips long enough for a gladius type sword. I realize that these were often stacked with several different thin pieces making up the overall cross section. I don't really mind the center strips losing some carbon over time and working, as I figure that is more true to original than perfect modern pattern welded.

Absence of evidence is not necessarily evidence of absence!
View user's profile Send private message
Michael Pikula
Industry Professional



Location: Madison, WI
Joined: 07 Jun 2008

Posts: 411

PostPosted: Thu 15 Jan, 2009 3:23 pm    Post subject:         Reply with quote

Depending on how many layers you are going for you should be able to get enough material for 2 twisted rods out of one billet that started out the size that I mentioned before, or more, depends on you and your set-up really.

Depending on your skill level, two billets should get you a Gladius type sword.
View user's profile Send private message Visit poster's website
Jeroen Zuiderwijk
Industry Professional



Location: Netherlands
Joined: 11 Mar 2005

Spotlight topics: 2
Posts: 740

PostPosted: Fri 16 Jan, 2009 1:12 am    Post subject:         Reply with quote

Michael Pikula wrote:
I don't know if it is historically to combine two billets to increase layer count and size, but I find it much better to work two billets and then weld them together if I need a larger billet. If you are working a huge billet you are going to end up fighting with it and might end up scraping more material and time then if you take your time, work small, and then add on to get the size/layers that you need.
I don't know about Roman patternwelding (there was a lot more variation in the early days of patternwelding), but according to Jaap Ypey it was pretty much standard to build the billet of 4 layers iron and 3 layers steel in the early medieval period. So that shows they're not doubled at least.
Jeroen Zuiderwijk
- Bronze age living history in the Netherlands
- Barbarian metalworking
- Museum photos
- Zip-file with information about saxes
View user's profile Send private message Visit poster's website


Display posts from previous:   
Forum Index > Off-topic Talk > pattern welding without strikers or trip hammer?
Page 1 of 1 Reply to topic
All times are GMT - 8 Hours

View previous topic :: View next topic
Jump to:  
You cannot post new topics in this forum
You cannot reply to topics in this forum
You cannot edit your posts in this forum
You cannot delete your posts in this forum
You cannot vote in polls in this forum
You cannot attach files in this forum
You can download files in this forum